Cathodic protection is key to ALWS

Letters

The article about steel corrosion in Lerwick Harbour (NCE 19 October) yet again illustrates the lack of knowledge and activity surrounding this subject.

Cathodic protection using either impressed currents or sacrificial anodes is the only sensible way of controlling this corrosion problem. All marine structures use cathodic protection but at the moment most are using the anodic corrosion sites to protect the rest of the steel. Repairing holes in sheet piling or spalling areas of concrete merely moves the corrosion to an adjacent site.

Many engineers treat cathodic protection as a black art and this ignorance is leaving us with embarrassingly large holes in our sheet piles and reinforced structures.

Ideally, cathodic protection should be installed on every marine structure during initial construction. The additional cost is minimal and could easily be offset by reducing sheet pile thicknesses (designed to corrode) or concrete cover/ quality (designed to protect).

John Drewitt, Concrete Repairs, Cathite House, 23a Willow Lane, Micham, Surrey, CR4 4TU

Have your say

You must sign in to make a comment

Please remember that the submission of any material is governed by our Terms and Conditions and by submitting material you confirm your agreement to these Terms and Conditions. Please note comments made online may also be published in the print edition of New Civil Engineer. Links may be included in your comments but HTML is not permitted.